Effect of pressurization profile on the deformation characteristics of fine-grained AZ31B Mg alloy sheet during gas blow forming

NCU Institutional Repository > 工學院 > 機械工程學系 > 期刊論文 > Item 987654321/50061

jsp.display-item.identifier=請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/50061

题名:	Effect of pressurization profile on the deformation characteristics of fine-grained AZ31B Mg alloy sheet during gas blow forming
作者:	Sun,PH;Wu,HY;Tsai,HH;Huang,CC;Tzou,MD
贡献者:	機械工程學系
关键词:	AL-ZN ALLOY;SUPERPLASTIC AA5083;ELEVATED-TEMPERATURES;MECHANISMS;BEHAVIOR;CREEP
日期:	2010
上传时间:	2012-03-27 17:02:34 (UTC+8)
出版者:	國立中央大學
摘要:	The deformation characteristics of a 0.6 mm-thick, fine-grained AZ31B Mg alloy sheet were investigated with the intention of reducing forming time during gas blow forming. The sheets were successfully deformed into hemispherical domes at 300, 370, and 420 degrees C under various pressurization profiles. The results show that the proposed pressurization profiles could achieve the goal of reducing forming time. A stepwise pressurization profile may be a suitable process at lower temperatures, whereas a constant or near constant pressure imposed during forming is a better method at higher temperatures. The pressurization profiles used in this study were not restricted to providing the optimum constant strain rate, which is often used in the traditional superplastic forming. Under the proposed pressurization profiles, maximum stress in the range of 23.5-45.6 MPa and resultant average strain rate in the range of 6.63 x 10(-3) to 1.56 x 10(-2) s(-1) were imposed on the deforming sheet at the apex of the dome. The pressurization profile might not be one of the major factors influencing formability at the same forming temperature but it can significantly affect the forming time. Deviation of the bulged shape from the perfect sphere shape increased with increasing forming temperature. (C) 2010 Elsevier B.V. All rights reserved.